Itme Number
|
Powder Type & Composition
|
Morphology
|
Properties & Industrial Application
|
Particle Size（um）
|
|
BS111-001
|
Al2O3 ≥99.5%
Fused
and Crushed
|
Angular Blocky
White
|
High hardness, excellent resistance to abrasive and sliding wear, erosion, cavitation and corrosion;
High dielectric strength, service temperatures: 1650 °C;
Used as hard face wear, fibre abrasion;
Particle erosion and high temperature erosion resistant coatings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS111-002
|
Al2O3 ≥99.95%
Agglomerated
And Sintered
|
Spheroidal
White
|
Excellent insulation and thermal insulation charateristics;
Wear resistant, chemically inert, stable under high temperature conditions;
For electronic and semiconductor production tools, biomedical implants;
Operating temperature up to 1650 °C;
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS112-001
|
Cr2O3 ≥99.5%
Fused
and Crushed
|
Angular Blocky
Dark green
|
Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear, erosion, cavitation and corrosion;
Coatings are insoluble in acids, alkalis and alcohol;
Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings;
Used on pump seal areas,grounds,rolls and wear rings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS112-002
|
Cr2O3 ≥99.95%
Agglomerated
and Sintered
|
Angular Blocky
Dark green
|
Tough, dense and smooth, high hardness, excellent resistance to sliding and abrasive wear, erosion, cavitation and corrosion;
Coatings are insoluble in acids, alkalis and alcohol;
Used as hard face wear, fibre abrasion, particle erosion, gas and liquid corrosion-resistant coatings;
Used on pump seal areas, grounds, rolls and wear rings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS113-005
|
TiO2 ≥99.7%
Sintered
and Crushed
|
Angular Blocky
Black
|
Tough and dense, high bonding strength,protection against high temperature oxidation, resistant to wear by abrasive grains and hard surfaces;
Moderate abrasive wear resistance;
Soluble in alkalis and sulfuric acid, but resistant to attack in many other environments;
Slightly conductive, static electricity does not build up on the coating surface.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS113-002
|
TiO2 ≥99.9%
Agglomerated
and Sintered
|
Spheroidal
Black
|
Tough and dense, high bonding strength, protection against high temperature oxidation, resistant to wear by abrasive grains and hard surfaces;
Moderate abrasive wear resistance;
Soluble in alkalis and sulfuric acid, but resistant to attack in many other environments;
Slightly conductive, static electricity does not build up on the coating surface.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS121-001
|
TiO2: 3%
Al2O3: Bal.
Fused
and Crushed
|
Angular Blocky
Black Grey
|
APS; Coatings are smooth and dense;
For use as corrosion, abrasion, erosion and sliding wear resistant coatings;
Typical applications in textile machines for guiding and handling of thread,rolls in paper industry,etc.;
Good dielectric strength at room temperatures, lower dielectric strength than pure Al2O3 coatings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS121-002
|
TiO2: 3%
Al2O3: Bal.
Agglomerated
and Sintered
|
Spheroidal
Yellow / Black
|
APS; Coatings are smooth and dense;
For use as corrosion,abrasion, erosion and sliding wear resistant coatings;
Typical applications in textile machines for guiding and handling of thread,rolls in paper industry,etc.;
Good dielectric strength at room temperatures,lower dielectric strength than pure Al2O3 coatings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS123-001
|
TiO2: 13%
Al2O3: Bal.
Fused
and Crushed
|
Angular Blocky
Black Grey
|
APS;High hardness, dense and smooth;
Excellent resistance to abrasive wear,erosion, corrosion and fretting;
High dielectric strength;
Used as hard face wear, fibre abrasion and particle erosion-resistant coatings.
|
-74/+38um
-45/+15um
-30/+10um
|
|
BS123-002
|
TiO2: 13%
Al2O3: Bal.
Agglomerated
and Sintered
|
Spheroidal
Yellow / Black
|
APS; High hardness, dense and smooth;
Excellent resistance to abrasive wear, erosion, corrosion and fretting;
High dielectric strength;
Used as hard face wear, fibre abrasion and particle erosion-resistant coatings.
|
-74/+38um
-45/+15um
-30/+10um
|